Thickness: 5mm - 70mm

Grade: 10CrNi2MoCu

Yield strength(MPA): 590 - 745

Product Detail | Technical Information | Packaging | More

Product Detail

Shanghai Metal Corporation is a professional manufacturer and supplier of 10CrNi2MoCu High Strength Weldable Alloy Steel Plate with high quality and reasonable price.

The 10CrNi2MoCu high strength weldable alloy steel plate has high strength, toughness, good weld ability, and resistance to seawater corrosion, but it also has a thickness span of 16-18 millimeters, which has good adaptability to shipbuilding technology. It is suitable for submarine pressure resistant shells, deep submergence lifeboats, large surface vessels, aircraft carriers, tank bridges, supersonic wind tunnels, and other engineering structures that require high strength and toughness.

If you want to know more about 10CrNi2MoCu High Strength Weldable Alloy Steel Plate price please feel free to contact us, we will reply you within 24 hours

Width: 1000mm - 2200mm or as customer request

Length: 6000mm - 12000mm or as customer request

Elongation rate δ (%): ≥ 16

Shrinkage rate ψ (%): ≥ 50

Standard: GJB 1663A-2005

1. Submarine pressure hull

2. Deep diving lifeboat

3. Large surface vessels

4. Aircraft carrier

Technical Information of 10CrNi2MoCu High Strength Weldable Alloy Steel Plate:

Grade	chemical composition
Grade	%C	%Si	%Mn	%P	%S	%Ni	%Cr	%Mo	%V	%Cu
10CrNi3MoV	0.06~0.11	0.17~0.37	0.3~0.6	≤0.015	≤0.010	2.60~3.00	0.90~1.20	0.20~0.27	0.04~0.10	-
10CrNi3MoCu	0.06~0.11	0.17~0.37	0.3~0.6	≤0.015	≤0.010	2.60~3.00	1.20~1.60	0.20~0.27	-	0.80~1.10
10CrNi2MoCu	0.06~0.11	0.17~0.37	0.3~0.6	≤0.015	≤0.010	2.60~3.00	2.00~2.30	0.17~0.25	-	0.80~1.10

Grade	Nominal thickness mm	Yield strength Mpa	Tensile strength Mpa	Elongation A%	Reduction Z%	Test temperature ℃	Impact absorbing energy AKV J	Fiber cross-sectional area FA%
10CrNi3MoV	11~35	590~730	≥655	≥16	≥50	-84	≥47	≥50
	11~35					-20	≥80	≥100
	10					-84	≥31	≥50
	10					-20	≥53	≥100
10CrNi3MoCu	36~70	510~650	-	≥16	≥50	-20	≥80	≥100
10CrNi2MoCu	5~9	510~670	-	≥16	-	-20	≥53	≥100

Packaging of 10CrNi2MoCu High Strength Weldable Alloy Steel Plate:

Products of Shanghai Metal Corporation are packed and labeled according to the regulations and customer's requests. Great care is taken to avoid any damage which might be caused during storage or transportation. In addition, clear labels are tagged on the outside of the packages for easy identification of the product I. D. and quality information.

1)SMC Standard

2)Customization

Notes:

1. The surface of the steel plate needs to undergo special treatments such as anti-corrosion coating and oil spray anti fouling layer to ensure the corrosion resistance and durability of the steel plate.

2. The thickness of the submarine shell steel plate is one of the key factors to ensure the safety of submarine navigation. If the shell steel plate is too thin, it is not only susceptible to damage from water pressure, impact and other factors, but also prone to hydraulic resonance caused by waves, flowing water and other eddy currents, leading to severe vibration of the submarine, and even causing equipment failures and accidents.

3. It is necessary to regularly check the shell for cracks, deformations, etc., and promptly repair and replace it to ensure the service life and safety of the submarine.