Standard: ASTM/ JIS/ GBT/ EN etc
Grade: EV-200/ EV-200F/ EV-200L
Thickness: 0.15mm - 2.0mm
Width: 600mm - 1500mm
Shanghai Metal Corporation is a leading PVC plastisol steel sheet manufacturer.
PVC plastisol steel is suitable to be used for roofing and siding in industrial or residential districts, especially in coastland with severe corrosion, chemical industrial district,or some environments that require high corrosion resistance. Due to its beautiful appearance, the product is suitable to be used for interior decoration (such as ceiling,partitions, fireproof boards, etc.), cases of electrical appliances (such as refrigerators, washing machines, vending machines, computers and their peripherals, walk-in coolers, refrigerated vehicles, etc.)
If you want to know more about PVC plastisol steel sheet, please feel free to contact us, we will reply you within 24 hours.
Technical Information of PVC Plastisol:
STANDARD SPECIFICATION |
SUBSTRATE |
EV-200 uses hot-dip galvanizedsteel sheets as its substrate. According to ASTMA 653M, coating mass is Z275(total both sides, 275g/m2 min.) |
EV-200F uses 5% Al-Zn alloycoated steel sheets as its substrate.Accordingto ASTMA 875M, coating mass is ZGF275(total both sides, 275g/m2 min.) |
EV-200L uses 55%Al-Zn alloycoated steel sheets as its substrate.Accordingto ASTM A 792M, coating mass is AZM150(totalboth sides,150g/m2 min.) |
PRE-TREATMENT |
Uses proper pre-treatment withexcellent corrosion resistance performance toform a conversion film on steel surface. |
COATING SYSTEM |
Two-sided 2C2B(2 Coat 2 Bake) coating systemis used. |
TOP PRIMER |
Polyurethane (PU) resin with high corrosionresistance is used as the top primer, with 4μm nominal dry film thickness. |
TOP COAT |
PVC Plastisol with high stability is used as the top coat,with 200μm nominal dry film thickness(the minimum triple-spot average coating filmthickness is 160μm). |
TOP COLOR & GLOSS |
Generally, top coat gloss is 20-40GU afterembossing (60°reflection angle,according to ASTM D 523) or subject to inquiry. |
BACK PRIMER |
PU resin with high corrosion resistance is used as the back primer,with 4μm nominal dry filmthickness. |
BCAKERCOAT |
There are two options of backercoat for ditterentapplications and environments. |
1.PVC Plastisol: lt is the same paint as top coatwithout embossing. The dry film thicknessis 100μm (the minimum triple-spot averagecoating film thickness is 70μm).The colorsare subject to inquiry. Roofing and siding forchemical plants should adopt this PVC double-sided product. |
2.Epoxy: The dry film thickness is 7μm. Color options include grayish brown or gray. It is suitable to be used for interior decoration,partitions,walk-in coolers,or roof,on which PU foaming thermal insulation materials are applied. |
3.Backercoat gloss is normally 25+ -7GU (60°reflection angle, according to ASTM D 523) |
Packaging of PVC Plastisol: