- Company overview The heart of SMC Vision & Philsophy Partnership Certifications Company culture
- Our service Design and Engineering Maintenance and Service Examine Production Line Upgrade and Transformation Storage and Logistics Processing, Trading and Distributor
- Management Our history Global responsibility Info Center
- Procurement center Internship
- Metal Steel Products Stainless Steel Products Aluminum Products Copper Products Galvanized Steel and PPGI Special Alloy Building Material
- Containers ISO Standard Container Equipment Container Storage Container Container House Refrigerated/Reefer Container Offshore Container Tank Container Container Fittings Container Trailer
- Gas Cylinder & Fire Extinguisher Cryogenic Liquid Cylinder Oxygen Gas Cylinder Storage Tank CNG Gas Cylinder LPG Gas Cylinder Hydrogen Gas Cylinder Nitrogen Gas Cylinder Industry Gas Cylinder Fire Extinguisher
- Metal Machinery Forming Machine Other Machinery Cutting Machine Processing Machine Bending Machine Block Machine Motor Spare Parts
- Mechanical Products Vehicle Industry Miscellany Mooring Equipment Marine Equipment Pressure Vessel Conveyor Belt Laser Equipment Bearing
- Electrical System Electrical Cable Automation Power Distribution Solar Power System Electric Protection System Transformer Production Line Lighting System
- Project Fiberglass Reinforced Plastic Plastic Pipes and Pipe Fittings Pontoon System
High Temperature Load-bearing Components of Aircraft Engines
Shape: Round bar, Flat bar, Sheet
Grade: X5NiCrTi26-15, 1.4980, UNS S666286, X6NiCrTiMoVB25-15-2, Grade660
Shanghai Metal Corporation is a professional manufacturer and supplier of High Temperature Load-bearing Components of Aircraft Engines with high quality and reasonable price.
The high temperature load-bearing components of aircraft engines mainly include key components such as turbine blades, guide vanes, combustion chambers, and turbine discs. These components are made of high-temperature alloy, usually with the grade X5NiCrTi26-15, 1.4944, UNS S666286, X6NiCrTiMoVB25-15-2, Grade660.
These metal materials have good high-temperature resistance, corrosion resistance, excellent weldability and processability, and have broad application scenarios.
Due to controlling the entire production process, we can provide stricter tolerances than other products. This saves time for our customers as our steel plates can be installed immediately after cutting without the need for leveling.
If you want to know more about High Temperature Load-bearing Components of Aircraft Engines price please feel free to contact us, we will reply you within 24 hours
Technical Information of High Temperature Load-bearing Components of Aircraft Engines:
|
Grade 660 Mechanical Properties |
||
|
Tensile Strength |
895 |
Mpa |
|
Yield Strength |
655 |
MPa |
|
Elongation After Fracture |
15 |
% |
|
Brinell Hardness |
248-341 |
HB |
|
X6NiCrTiMoVB25-15-2 Mechanical Properties |
||
|
Proof Strength |
600 |
Mpa |
|
Tensile Strength |
900-1150 |
MPa |
|
Elongation After Fracture |
15 |
% |
|
Impact energy (ISO-V) At 20°C |
50 |
J |
|
Chemical Composition % |
||||||||||||
|
Grade |
C |
Si |
Mn |
P |
S |
Al |
B |
Cr |
Mo |
Ni |
V |
Others |
|
X6NiCrTiMoVB25-15-2 |
0.03-0.08 |
≤1.00 |
1.00-2.00 |
≤0.025 |
≤0.015 |
≤0.35 |
0.003-0.010 |
13.5-16.0 |
1.0-1.5 |
24.0-27.0 |
0.10-0.50 |
Ti:1.90-2.30 |
|
Grade 660 |
≤0.08 |
≤1.00 |
≤2.00 |
≤0.04 |
≤0.03 |
≤0.35 |
0.001-0.010 |
13.5-16.0 |
1.0-1.5 |
24.0-27.0 |
0.10-0.50 |
Ti:1.90-2.35 |
Packaging of High Temperature Load-bearing Components of Aircraft Engines:
Shanghai Metal Corporation Products are packed and labeled according to the regulations and customer's requests. Great care is taken to avoid any damage which might be caused during storage or transportation. In addition, clear labels are tagged on the outside of the packages for easy identification of the product I. D. and quality information.
1)SMC Standard
2)Customization
here
for
price